1. A preparation method of peptide-crosslinked protein-imprinted polymer comprising the steps of: 1) a main monomer, functional monomers, a peptide crosslinking agent and a template protein are dissolved in an aqueous solution to obtain a mixed solution; 2) an initiator or initiator system is added to the mixed solution described in the step 1) to initiate the polymerization when the peptide crosslinking agent exists in a helix conformation, thereby obtaining a polymer; 3) the template protein is eluted when the peptide chain exists in a coil conformation and a peptide-crosslinked protein-imprinted polymer is obtained; the peptide crosslinking agent is a peptide with a polymerizable double bond at its both ends, and being capable of undergoing helix-coil transition.

2. The preparation method according to claim 1, which is characterized in that the number of amino acids in the peptide crosslinking agent is 2 to 100.

3. The preparation method according to claim 1, which is characterized in that the number of amino acids in the peptide crosslinking agent is 5 to 30.

4. The preparation method according to any one of claims 1 to 3, which is characterized in that the aqueous solution described in the step 1) includes one of phosphate buffer, Tris buffer and NaClO4 solution.

5. The preparation method according to claim 1, which is characterized in that the mass ratio of the main monomer: the functional monomers : the peptide crosslinking agent : the template protein described in the step 1) is (10-30) : (0.5-2) : (5-20) : (5-20).

6. The preparation method according to claim 1, which is characterized in that the initiator or initiator system is selected from ammonium persulfate/tetramethylethylenediamine, ammonium persulfate/sodium bisulfite, potassium persulfate/tetramethylethylenediamine, and potassium persulfate/sodium bisulfite.

7. The preparation method according to claim 1, which is characterized in that the conformational state of the peptide crosslinking agent is detected by circular dichroism (CD), in which CD spectrum presents a negative peak at 222 nm and 208 nm, and a positive peak at 190 nm±5 nm representative of a helix conformation; also, CD spectrum presents a negative peak at 199 nm, and a positive peak at 220 nm±5 nm representative of a coil conformation.

8. A peptide-crosslinked protein-imprinted polymer prepared by the preparation method according to any one of claims 1 to 7.

9. An application of the peptide-crosslinked protein-imprinted polymer according to claim 8 in protein enrichment, separation and purification.

10. The application according to claim 9, which is characterized in that the peptide-crosslinked protein-imprinted polymer is used to adsorb target protein when the peptide chain exists in a helix conformation and to elute target protein when the peptide chain exists in a coil conformation.

[0001]The application claims the priority of China patent application No. 201910147938.9, named "Peptide-crosslinked Protein-imprinted Polymers And Preparation Method And Applications Thereof , filed on Feb. 28, 2019 to National Intellectual Property Administration, PCR.

TECHNICAL FIELD

[0002]The invention belongs to the technical field of bioseparation engineering, and especially relates to peptide-crosslinked protein-imprinted polymers and preparation method and applications thereof.

BACKGROUND

[0003]Molecularly imprinted polymers are a class of artificial receptors inspired by antibody which can recognize antigen specifically. Molecularly imprinted polymers have benefits such as simple preparation, good stability and low cost as compared to natural receptors like antibody, playing a significant role in the field of environmental science, life science, etc. The general processes of molecular imprinting are as follows: (1) the polymer is synthesized by polymerization of monomers and cross-linkers in the presence of template molecules; (2) the template is removed, leaving imprint cavities, which are chemically and sterically complementary to the template molecule, in the polymer; (3) the imprinted polymer recognize and selectively recombine target molecules when exposed to a solution containing the template molecules.

[0004]The imprinting of low molecular-weight compounds has gained great success. However, the imprinting of high molecular-weight biomacromolecules, particularly proteins still faces many challenges. The first problem faced by protein imprinting is the difficulty in template removal. The high molecular weights of the template proteins severely retard their diffusion through the dense polymer networks. Presently, the template proteins were usually removed by harsh methods, for example, elution using high concentration salt solutions (e.g. 1M NaCl) or mixed solutions of acetic acid/surfactant (SDS or Tween-20) (a common formula is 10% SDS/10% AcOH). Proteinase is also used to digest template proteins for removing these template proteins. These treatments cannot guarantee a complete removal of the template proteins, and often cause problems such as changes in structure of the imprinted polymer networks, non-specific adsorption of the proteins, and blockage of the imprinting sites. More importantly, the stringent elution conditions are so easy to cause denaturation and deactivation of the template proteins that the eluted target proteins lose their use values, while the method by digestion with proteinase directly destroys the template proteins. In many applications of protein imprinting, such as enrichment, separation and purification of proteins, it is necessary to recover active target proteins, so the harsh elution conditions make such imprinted polymers largely lose their application values.

[0005]A second serious problem of protein imprinting is a poor imprint effect. Proteins are only soluble in water and are easy to denature and deactivate, so the organic solvents often used in the imprinting of low molecular weight compounds are not applicable, and the imprinting of protein can be only performed in an aqueous solution. On the one hand, this limits the selection of monomer; on the other hand, the presence of water weakens the hydrogen bonding between the template and the functional monomer, resulting in a reduction of acting force between the template and the functional monomer. To recognize the target molecule, the size and spatial configuration of imprinting sites in the polymer must be kept unchanged. Therefore, the degree of cross-linking of the polymer in small molecule imprinting is often up to more than 50%. However, in protein imprinting, the templates are so difficult to remove that a low degree of cross-linking can only be used. Given these reasons, the imprinting effect of existing protein-imprinted materials is not ideal. For example, Chen, et al. disclosed an imprinted polymer using lysozyme as the template protein, the imprinted polymer was polymerized by using N-isopropylacrylamide as the main monomer, methacrylic acid and acrylamide as the functional monomers, and N,N'-methylenebisacrylamide as cross-linker whose content was 3.11 mol%. The template protein was eluted by using 1M NaCl. The imprinting capacity Qm was 350 mg/g dry gel and the imprinting factor was 1.167 (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77).

[0006]For protein imprinting, the problems of difficulty in template removal and poor imprint effect seem to be intrinsic problems, and these two problems are mutually restrained and difficult to solve at the same time. A long-term study still does not find an effective method to solve these problems, casting a shadow on the prospect of protein imprinting. (Culver, H. R.; Peppas, N. A., Chemistry of Materials, 2017, 29(14), 5753-5761).

SUMMARY

[0007]In view of this, the objective of the invention is to provide peptide-crosslinked protein-imprinted polymers and preparation method and applications thereof.

[0008]To achieve the above-mentioned objective of the invention, the invention provides the following technical solutions: A preparation method of peptide-crosslinked protein-imprinted polymer comprising the steps of:

1) a main monomer, functional monomers, a peptide crosslinking agent and a template protein are dissolved in an aqueous solution to obtain a mixed solution; 2) an initiator or initiator system is added to the mixed solution described in the step 1) to initiate the polymerization when the peptide crosslinking agent exists in a helix conformation, thereby obtaining a polymer; 3) the template protein is eluted when the peptide chain exists in a coil conformation and a peptide-crosslinked protein-imprinted polymer is obtained;

the peptide crosslinking agent is a peptide with a polymerizable double bond at its both ends, and being capable of undergoing helix-coil transition.

[0009]Preferably, the number of amino acids in the peptide crosslinking agent is 2 to 100.

[0010]Preferably, the number of amino acids in the peptide crosslinking agent is 5 to 30.

[0011]Preferably, the aqueous solution used to prepare the mixed solution as described in the step 1) includes one of phosphate buffer, Tris buffer and NaClO 4 solution.

[0012]Preferably, the mass ratio of the main monomer: the functional monomer: the peptide crosslinking agent : the template protein described in the step 1) is (10-30) : (0.5-2) : (5-20) : (5-20).

[0013]Preferably, the initiator or initiator system is selected from ammonium persulfate/tetramethylethylenediamine, ammonium persulfate/sodium bisulfite, potassium persulfate/tetramethylethylenediamine, and potassium persulfate/sodium bisulfite.

[0014]Preferably, the conformational state of the peptide crosslinking agent is detected by circular dichroism (CD) , in which CD spectrum presents a negative peak at 222 nm and 208 nm, and a positive peak at 190 nm±5 nm representative of a helix conformation; also, CD spectrum presents a negative peak at 199 nm, and a positive peak at 220 nm±5 nm representative of a coil conformation.

[0015]The invention provides a peptide-crosslinked protein-imprinted polymer prepared by said preparation method.

[0016]The invention provides the application of said peptide-crosslinked protein-imprinted polymer in protein enrichment, separation and purification.

[0017]Preferably, the peptide-crosslinked protein-imprinted polymer is used to adsorb target protein when the peptide crosslinking agent exists in a helix conformation and to elute target protein when the peptide crosslinking agent exists in a coil conformation.

[0018]The benefits of the invention: The peptide crosslinking agent can transit between different conformations in response to changes in external conditions. Given this special property, the preparation method of peptide-crosslinked protein-imprinted polymer provided in the invention uses the peptide crosslinking agent instead of traditional cross-linking reagent (such as N,N'-methylenebisacrylamide) to conduct polymerization when the peptide crosslinking agent exists in a helix conformation and template elution when the peptide crosslinking agent exists in a coil conformation. When the peptide crosslinking agent transits from a helix conformation to a coil conformation, the protein-imprinted polymers swell which facilitates the removal of the template protein. Therefore the removal of template proteins under mild conditions is achieved. When the peptide-crosslinked protein-imprinted polymer is applied, the peptide crosslinking agent is re-transformed from a coil conformation to a helix conformation by adjusting external environmental parameters, and the whole protein-imprinted polymer shrink; more importantly, since the conformation transition is highly specific when peptide folds back from a coil conformation into a helix conformation, the size and shape of the imprint cavities in the protein-imprinted polymer can completely recover and thus can specifically recognize the target protein.

[0019]The peptide-crosslinked protein-imprinted polymer provided in the invention not only can completely remove the template protein under mild conditions, but also can significantly improve the imprint effect of the protein-imprinted polymer. According to the description of example 1, the method described in the invention was used to prepare the protein-imprinted polymer which had the same formula with the protein-imprinted polymer with lysozyme as template described in the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77), in which the content of the cross-linking reagent was still 3.1 mol%, but the common cross-linking reagent N,N'-methylenebisacrylamide was replaced by the peptide crosslinking agent described in example 1. The template protein was removed completely by elution with a pH 7.4 phosphate buffer (containing 0.154M NaCl). Protein rebinding demonstrated that the adsorption capacity Qm and imprinting factor of the newly synthesized imprinted polymers were 679 mg/g dry gel and 10.0, respectively, while the adsorption capacity Qm and imprinting factor of the imprinted polymer described in the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77) were 350mg/g dry gel and 1.167, respectively. As compared to the reference, the imprint effect of the peptide-crosslinked imprinted polymer was improved significantly.

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] Fig.1 is CD spectra of the peptide-crosslinked protein-imprinted polymer in example 1 under different conditions showing a reversible helix-coil transition of the peptide chain in the polymer; Fig.2 is adsorption isotherms of the template protein on peptide-crosslinked protein-imprinted polymer (MIP) and the corresponding non-imprinted polymer (NIP). Fig.3 is adsorption of lysozyme (Lys), the template protein, and various other proteins on the peptide-crosslinked protein-imprinted polymer (MIP) and the corresponding non-imprinted polymer (NIP). Fig. 4 is the bioactivities of lysozyme samples (related to native lysozyme) which samples were eluted using a low-salt eluant and a high salt eluant. Fig. 5 is results of SDS-PAGE analysis of the lysozymes extracted from egg white, in which the first lane is a lysozyme specimen, the second lane is an untreated egg white sample, the third lane is an egg white sample treated with the peptide-crosslinked protein-imprinted polymer, and the fourth lane is an eluent sample obtained by treating egg white with the peptide-crosslinked protein-imprinted polymer followed by elution with a low-salt eluent.

DESCRIPTION OF THE EMBODIMENTS

[0021]The invention provides a preparation method of peptide-crosslinked protein-imprinted polymer, which comprises the steps of: 1) a main monomer, functional monomers, a peptide crosslinking agent and a template protein are dissolved in an aqueous solution to obtain a mixed solution; 2) an initiator or initiator system is added to the mixed solution described in the step 1) to initiate the polymerization when the peptide crosslinking agent exists in a helix conformation, thereby obtaining a polymer; 3) the template protein is eluted when the peptide chain exists in a coil conformation and a peptide-crosslinked protein-imprinted polymer is obtained; the peptide crosslinking agent is a peptide with a polymerizable double bond at its both ends, and being capable of undergoing helix-coil transition.

[0022]In the invention, the peptide crosslinking agent is a peptide with a polymerizable double bond at its both ends, and being capable of undergoing helix-coil transition. In the invention, the helix-coil transition preferably occur under different conditions; during the detailed implementation of the invention, the helix-coil transition may be triggered by temperature change, pH value change, and ionic strength change, etc. The invention poses no special requirements on the conditions of helix-coil transition, and these conditions are determined depending on the type of different peptide crosslinking agents, as long as the helix-coil transition can be achieved. In the invention, the conformation of the peptide chain is detected by circular dichroism, in which CD spectra present a negative peak at 222 nm and 208 nm, and a positive peak at 190 nm±5 nm representative of a helix conformation; also, CD spectrum presents a negative peak at 199 nm, and a positive peak at 220 nm±5 nm representative of a coil conformation.

[0023]The invention poses no special requirements on the number, type, and sequence of amino acids in said peptide crosslinking agent, and any peptide with a polymerizable double bond at its both ends, and being capable of undergoing helix-coil transition can be used as the peptide crosslinking agent described in the invention. During the detailed implementation of the invention, the number of amino acids in the peptide crosslinking agent is 2 to 100, preferably 5 to 30. The peptide crosslinking agent described in the present embodiment can be selected from the peptides having a structure of formula I to VI described below:

[0024]The invention dissolves a main monomer, functional monomers, a peptide crosslinking agent and a template protein in an aqueous solution to obtain a mixed solution. The invention poses no special requirements on the type of the main monomer and functional monomers, and the conventional main monomers and functional monomers used in the preparation of protein-imprinted polymers in the art may be used. The invention poses no special requirements on the type of template proteins, any type of proteins can be used as the template protein. In the invention, the aqueous solution preferably includes but are not limited to one of phosphate buffer, Tris buffer and NaClO 4 solution; and the preferred concentration and pH value of the aqueous solution described in the invention are determined depending on the type of the aqueous solution and the specific type of the peptide crosslinking agent. When the aqueous solution is phosphate buffer, the concentration of the phosphate buffer is preferably 1-100 mmol/L, more preferably 10-20 mmol/L, and the pH value of the phosphate buffer is preferably 5.0-5.6. When the aqueous solution is Tris buffer, the concentration of the phosphate buffer is preferably 1-50 mmol/L, more preferably 10-20 mmol/L, and the pH value of the Tris buffer is 7.0-10. When the aqueous solution is NaClO 4 solution, the concentration of the NaClO 4 solution is 0.05-0.50 mol/L, more preferably 0.1-0.3 mol/L. In the invention, the mass ratio of the main monomer : the functional monomers : the peptide crosslinking agent : the template protein is preferably (10-30) : (0.5-2) : (5-20) : (5-20). In the invention, the ratio of total mass of the main monomer, the functional monomers, the peptide crosslinking agent, and the template protein to the volume of the aqueous solution is preferably (1-5) : (5-15).

[0025]In the invention, an initiator is added to the mixed solution after obtaining the mixed solution to polymerize when the peptide crosslinking agent exists in a helix conformation, thereby obtaining a polymer. In the invention, the initiator or initiator system is preferably selected from ammonium persulfate/ tetramethylethylenediamine, ammonium persulfate/sodium bisulfite, potassium persulfate/tetramethylethylenediamine, and potassium persulfate/sodium bisulfite; more preferably, ammonium persulfate/tetramethylethylenediamine. When ammonium persulfate/tetramethylethylenediamine are selected as the initiator, the mass concentration of the ammonium persulfate solution is preferably 1-20%, more preferably 5-10%, and the volume ratio of the ammonium persulfate solution to tetramethylethylenediamine is preferably (8-12) : 1, more preferably 10:1. In the invention, the volume ratio of the mixed solution to the initiator is preferably (25-50) : (1-5). In the invention, the polymerization time is preferably 20-28 h, more preferably 24 h; and the polymerization temperature is adjusted correspondingly depending on the type of the specific peptide crosslinking agent to enable the peptide crosslinking agent exists in a helix conformation.

[0026]In the invention, after obtaining the polymer, the template protein is removed when the peptide chain exists in a coil conformation to obtain a peptide-crosslinked protein-imprinted polymer. In the invention, the eluent used in elution is preferably consistent with the corresponding aqueous solution, and the pH or temperature of the elution is different from that during the polymerization. The invention poses no special requirements on elution conditions, as long as these conditions enable the peptide chain exists in a coil conformation.

[0027]The invention provides peptide-crosslinked protein-imprinted polymers prepared by said preparation method.

[0028]The invention provides applications of said peptide-crosslinked protein-imprinted polymer in protein enrichment, separation and purification. In the detailed implementation of the invention, the peptide-crosslinked protein-imprinted polymer is used to adsorb target protein when the peptide chain exists in a helix conformation and target protein is eluted when the peptide chain exists in a coil conformation.

[0029]The following described the technical solutions provided in the invention in detail in combination with embodiments, but should not be understood as limiting the protection scope of the invention.

Example 1

[0030]The synthesis of imprinted polymers: 200 mg of N-isopropylacrylamide, 5 mg of acrylamide, 4 µL of methacrylic acid, 115 mg of the peptide crosslinking agent, and 100 mg of template protein lysozyme were dissolved in 2 mL of a 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µL of 10% APS and 5 µL of TEMED were added to initiate polymerization, and the reaction was carried out at 37 °C for 24 hours to obtain the imprinted polymer MIP. The preparation of non-imprinted polymer NIP is the same as that of imprinted polymer, except that no template protein lysozyme is added. The structure of the peptide crosslinking agent is as shown in Formula I:

The elution of template protein:

[0031]Protein elution was performed at 37 °C with a 20 mM pH 7.4 phosphate buffer solution (containing 0.154 M NaCl to simulate a physiological ionic strength). The absorbance values of eluent were determined, and an ultraviolet spectrophotometer was used to draw a standard curve of absorbance-concentration of target protein at specific wavelengths. The absorbance values of protein solution were converted into concentration values according to the standard curve. The results were as follows: 100 mL of the eluent was used each time. The concentration of template protein in the eluent after the first elution was 0.927 mg/mL; the concentration of template protein in the eluent after the second elution was 0.0474 mg/mL; the concentration of template protein in the eluent after the third elution was 0.0037 mg/mL; while the template protein was not detected in the eluent by an ultraviolet spectrophotometer after the fourth elution. Elution rate = total amount of eluted protein / total amount of imprinted protein, in which the total amount of imprinted protein was 100 mg, and the elution rate was 97.8%. Finally, the imprinted polymer was washed with deionized water to remove residual sodium chloride.

Study of imprint effect:

[0032]A various concentrations of lysozyme solutions were formulated with a 20 mM pH 5.5 phosphate buffer solution. MIP or NIP was added at 37°C. After thorough adsorption, an ultraviolet spectrophotometer was used to detect the concentration of lysozyme in the supernatant and calculate adsorption amount. The calculation of adsorption amount was performed using a conventional calculation method in the art, see reference Z. Hua, et al. Langmuir, 2008, 24, 5773-5780. The adsorption isotherms (adsorption amount v.s. equilibrium concentration of protein) were drawn, and theses curves were fitted by Langmuir model. The results showed that the adsorption capacity Qm and imprinting factor of MIP were 679 mg/g dry gel and 10.0, respectively. The formula of this embodiment was the same as that of the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77), except that an equal molar amount of peptide crosslinking agent was used to replace the crosslinking agent used in the reference. The adsorption capacity Qm and imprinting factor of the imprinted polymer described in the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77) were 350mg/g dry gel and 1.167, respectively. As compared to the reference, the imprint effect of the imprinted polymer prepared by this embodiment was improved significantly.

[0033]20 mM of a pH 5.5 phosphate buffer solution was used to prepare various protein solutions with a concentration of 0.4 mg/mL, including lysozyme, cytochrome C (Cyt C), hemoglobin (Hb), horseradish peroxidase (HRP), bovine serum albumin (BSA), trypsin inhibitor (Try). MIP or NIP was added at 37°C. After thorough adsorption, the absorbance value of supernatant was detected by UV and the adsorption amount was calculated. The imprinting factors of various proteins were 10.48 (Lysozyme), 3.70 (Cyt C), 1.15 (Hb), 1.57 (HRP), 1.02 (BSA), and 1.24 (Try) , indicating that the imprinted polymer can selectively adsorb lysozyme.

Comparative example 1

The synthesis of imprinted polymers:

[0034]200 mg of N-isopropylacrylamide, 5 mg of acrylamide, 4 µL of methacrylic acid, 9 mg N, N'-methylenebisacrylamide (BIS), and 100 mg of template protein lysozyme were dissolved in 2 mL of a 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µL of 10% APS and 5 µL of TEMED were added to initiate polymerization, and the reaction was carried out at 37 °C for 24 hours to obtain the imprinted polymer MIP. The preparation of non-imprinted polymer NIP is the same as that of imprinted polymer, except that no template protein lysozyme is added. The formula was completely the same as that of the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77). The only difference was that the peptide crosslinking agent was replaced by an equal molar amount of a common cross-linking agent N, N'-methylenebisacrylamide as compared to the formula of imprinted polymer in example 1.

The elution of template protein:

[0035]Protein elution was performed at 37°C with a 20 mM pH 7.4 phosphate buffer solution (containing 0.154 M NaCl to simulate physiological ionic strength). The first elution rate was 35.77%, the second elution rate was 5.52%, the third elution rate was 2.85%, and the fourth elution rate was 0. The total elution rate was 44.14%. The results indicated that more than half of the template proteins could not be eluted under this condition. Whereas, for the peptide-crosslinked imprinted polymers prepared in example 1, the template protein was able to be completely eluted under the same condition.

[0036]To compare with the imprint experiments of the protein-imprinted polymer synthesized with the peptide crosslinking agent, the proteins were eluted with a 20 mM pH7.4 phosphate buffer solution containing 1M NaCl at 37°C until the remaining template proteins were completely eluted.

Study of imprint effect:

[0037]MIP was protein-eluted with a 20 mM pH 7.4 phosphate buffer solution containing 1 M NaCl to completely remove the template protein. A various concentrations of lysozyme solutions were formulated with a 20 mM pH 5.5 phosphate buffer solution. MIP or NIP was added at 37°C. After thorough adsorption, an ultraviolet spectrophotometer was used to detect the concentration of lysozyme in the supernatant and calculate adsorption amount. The calculation of adsorption amount was performed using a conventional calculation method in the art, see reference Z. Hua, et al. Langmuir, 2008, 24, 5773-5780. The adsorption isotherms (adsorption amount v.s. equilibrium concentration of protein) were drawn, and theses curves were fitted by Langmuir model. The results showed that the adsorption capacity Qm of MIP was 387.0 mg/g dry gel, and the maximum adsorption capacity Qm of NIP were 210.9 mg/g dry gel, and imprinting factor was 1.83. The results were similar to the results reported in the reference (Z. Chen, et al. Journal of Molecular Recognition, 2008, 21(1), 71-77).

[0038]The formula of comparative example 1 was substantially the same as that of example 1, the only difference is that comparative example 1 used a common crosslinking agent N, N-methylenebisacrylamide, while example 1 used an equal molar amount of the peptide crosslinking agent. It can be seen that the use of peptide crosslinking agent not only can achieve complete removal of template protein under mild conditions and can also improve imprint effect significantly.

Example 2

The synthesis of imprinted polymer:

[0039]200 mg of N-isopropylacrylamide, 2.5 mg of acrylamide, 8 µL of dimethylaminoethyl methacrylate, 115 mg of the peptide crosslinking agent, and 100 mg of template protein bovine serum albumin (BSA) were dissolved in 2 mL of 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µL of 10% APS and 5 µL of TEMED were added to initiate the polymerization. The reaction was carried out at 37 °C for 24 h to obtain the imprinted polymer MIP. The preparation of non-imprinted polymer NIP is the same as that of imprinted polymer, except that no template protein bovine serum albumin is added. The structure of peptide crosslinking agent is the same as that in example 1.

The elution of template protein:

[0040]Protein elution was performed at 37°C with a 20 mM pH 7.4 phosphate buffer solution (containing 0.154 M NaCl to simulate physiological ionic strength), and four elution rates were 95.24%, 2.05%, 0.24%, 0%, respectively. The total elution rate was 97.51%. Finally, the imprinted polymer was washed with deionized water to remove residual salts.

Study of imprint effect:

[0041]A various concentrations of BSA solutions were formulated with a 20 mM pH 5.5 phosphate buffer solution. MIP or NIP was added at 37°C. After thorough adsorption, an ultraviolet spectrophotometer was used to detect the concentration of template protein bovine serum albumin in the supernatant. The adsorption isotherms (adsorption amount v.s. equilibrium concentration of protein) were drew, and theses curves were fitted by Langmuir model. The results showed that the maximum adsorption capacity Qm of MIP was 420.3 mg/g dry gel, the maximum adsorption capacity Qm of NIP was 54.4 mg/g dry gel, the imprinting factor was 7.72.

Comparative example 2

The synthesis of imprinted polymers:

[0042]200 mg of N-isopropylacrylamide, 2.5 mg of acrylamide, 8 µL of dimethylaminoethyl methacrylate, 9 mg of N, N'-methylenebisacrylamide, and 100 mg of template protein bovine serum albumin (BSA) were dissolved in 2 mL of a 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µl of 10% APS and 5 µL of TEMED were added to initiate the polymerization. The reaction was carried out at 37 °C for 24 h to obtain the imprinted polymer MIP. The preparation of non-imprinted polymer NIP is the same as that of imprinted polymer, except that no template protein bovine serum albumin was added.

The elution of template protein:

[0043]Protein elution was performed at 37°C with a 20 mM pH 7.4 phosphate buffer solution (containing 0.154 M NaCl to simulate physiological ionic strength). The first elution rate was 54.77%, the second elution rate was 6.96%, the third elution rate was 0.75%, and the fourth elution rate was 0. The total elution rate was 62.48%. The results indicated that there were substantial template proteins could not be eluted under this condition. Whereas, for the peptide-crosslinked imprinted polymers prepared in embodiment 2, the template proteins was able to be completely eluted under the same condition.

[0044]The proteins were eluted with a 20 mM pH 7.4 phosphate buffer solution containing 1M NaCl at 37°C until the template proteins were completely eluted.

Study of imprint effect:

[0045]MIP was protein-eluted with a 20 mM pH 7.4 phosphate buffer solution containing 1 M NaCl to completely remove the template protein. A various concentrations of BSA solutions were formulated with a 20 mM pH 5.5 phosphate buffer solution. MIP or NIP was added at 37°C. After thorough adsorption, an ultraviolet spectrophotometer was used to detect the concentration of template protein bovine serum albumin in the supernatant and to calculate the adsorption amount. The adsorption isotherms (adsorption amount v.s. equilibrium concentration of protein) were drew, and theses curves were fitted by Langmuir model. The results showed that the maximum adsorption capacity Qm of MIP was 214.7 mg/g dry gel, and the maximum adsorption capacity Qm of NIP was 126.3 mg/g dry gel, the imprinting factor was 1.69.

[0046]The formula of comparative example 2 was substantially the same as that of example 2, the only difference is that comparative example 2 used a common crosslinking agent N, N-methylenebisacrylamide, while example 2 used an equal molar amount of the peptide crosslinking agent. It can be seen that the use of peptide crosslinking agent not only can completely remove template protein under mild conditions and can also improve imprint effect significantly.

Example 3

The synthesis of imprinted polymers:

[0047]200 mg of N-isopropylacrylamide, 5 mg of acrylamide, 4 µL of methacrylic acid, 51.74 mg of the peptide crosslinking agent, and 100 mg of template protein cytochrome C (Cyt C) were dissolved in 2 mL of 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µL of 10% APS and 5 µL of TEMED were added to initiate the polymerization. The reaction was carried out at 37°C for 24 h to obtain the imprinted polymer MIP. The preparation of non-imprinted polymer NIP was the same as that of imprinted polymer, except that no template protein cytochrome C was added. The structure of peptide crosslinking agent is the same as that in example 1.

The elution of template protein:

[0048]Protein elution was performed at 37°C with a 20 mM pH 7.4 phosphate buffer solution (containing 0.154 M NaCl to simulate physiological ionic strength), and four elution rates were 93.40%, 2.06%, 1.34%, 0%, respectively. The total elution rate was 96.8%. Finally, the imprinted polymer was washed with deionized water to remove residual salts.

Study of imprint effect:

[0049]A various concentrations of Cyt C solutions were formulated with a 20 mM pH 5.5 phosphate buffer solution. MIP or NIP was added at 37 °C. After thorough adsorption, an ultraviolet spectrophotometer was used to detect the concentration of template protein cytochrome C in the supernatant. The adsorption isotherms (adsorption amount v.s. equilibrium concentration of protein) were drawn, and theses curves were fitted by Langmuir model. The results showed that the maximum adsorption capacity Qm of MIP was 562.0 mg/g dry gel, and the maximum adsorption capacity Qm of NIP was 79.6 mg/g dry gel, and imprinting factor was 7.1.

Comparative example 3

The synthesis of imprinted polymers:

[0050]200 mg of N-isopropylacrylamide, 5 mg of acrylamide, 4 µL of methacrylic acid, 4 mg of N, N'-methylenebisacrylamide, and 100 mg of template protein cytochrome C (Cyt C) were dissolved in 2 mL of 20 mM pH 5.5 phosphate buffer solution. After thorough mixing, 50 µl of 10% APS and 5 µL of TEMED were added to initiate the polymer